Corrosion Protection is an area that is utmost concern especially with regards to assets continuity and preservation. In line with our expertise and experience, we have developed and patented a product that meets such critical demands and conditions. Product Characteristics
A low viscosity, non-solvent type 100% volume solid epoxy coating with excellent adhesion to steel, concrete, metal to metal
and non-ferrous metals such as aluminium, stainless steel, titanium FRP and even glass. It can be applied in harsh and adverse conditions for e.g., tidal zone areas, underwater applications and also to oily surfaces which gives simplicity of application to the applicator with minimum surface preparation. Versatile in which it can be applied onto wet or dry surfaces and displays excellent adhesion and compatibility to other coatings. Contains Zirconium and is suitable for rebuilding pitted surfaces up to 5mm. Solvent free system that is ideal for use for interior of drinking water tanks. The coating is suitable for use on the floor and interior for the food processing and manufacturing industry, Oil & Gas and power industry. Product Information
Colour Black, Grey, White and Yellow
Packing Size 10-kg and 20-kg pack
Non-Volatile Content 100%
Mixing Ratio Epoxy and Hardener (5:1) by Weight only
Full Cure 30°c in 48 Hours
Pot Life 30 to 40 mins at 30°c
Touch Dry 3 Hours with Walkover of 4 to 8 hours at 30°c
Temperature Resistance 5°c - 150°c
Chemical Resistance 75% H2SO4
Volume Solid 100%
Recommended DFT 100 - 200 µm
Coating Layer 1-2
Theoretical Coverage 10m2/litre (at DFT 100 µm ) * Allow for Application losses and Surface irregularities
Shelf Life At least 24 months when stored in sealed containers
Application Area
Tanks, Exterior of Steel and Iron Pipes
Coating onto GRE / Fiber Glass
Offshore structures, marine vessels, FPSO
Vessel linings under immersed conditions up to 150°C
Concrete Structures
Splash Zones, Tidal Zones, Flow Lines, Risers, Jetty's
Water Storage Tanks
Fishing Boats, Ships & Barges
Water Proofing
Gratings with minimum surface preparation
Bridges, Walkways, Bridge bearings, Railings
Decks, piping, storage tanks, ballast tanks
Acid Linings subject to type of acids
Concrete Repairs
Pressure Vessels, Storage Tanks, Turbine Ducts / Exhaust
Wooden Blocks, Glass, Stainless Steel Products
Industrial Floor Coatings
Roads (Zebra Crossing, Divider's etc..) Environmental
Blasting or application should NOT be carried out when:
Relative humidity is >95%
Substrate temperature below 4°C.